Photoionization of Polyvalent Ions

Engelsk Paperback
Se mere i:

Photoionization of Polyvalent Ions

Engelsk Paperback

515 kr
Tilføj til kurv
Sikker betaling
23 - 25 hverdage

Om denne bog
The effect of polyvalent dopants on photoinduced defect formation was studied in different glasses. Ionisation of the glass matrix results in intrinsic defects, positively charged hole and negatively charged electron centres. Polyvalent dopants can be photooxidised or photoreduced. These extrinsic defects might replace selectively one or several intrinsic defects and/or cause an increase in the number of opposite charged defects. Photoionisation can also result in unusual dopant valences otherwise not observed in glasses. The systematic comparison of different dopants and glass systems irradiated by excimer lasers helps to understand defect generation processes and might eventually help in the design of UV-resistant or UV-sensitive glasses. Defect formation occurs in the ppm range and was analysed by optical and EPR spectroscopy. A series of polyvalent dopants such as typical trace impurities, glass or melt additives and typical dopants used for optical components like filter glasses, optical sensors, fluorophores or photochromes, were studied. Distinct melting conditions give rise to different valences of various dopants and as a consequence different photoinduced redox-reactions might be observed after irradiation. Some dopants are photooxidised while others are photoreduced Some defects recombine easily or transform into more stable defects while others are stable for months or years.
Product detaljer
Sprog:
Engelsk
Sider:
82
ISBN-13:
9781607410713
Indbinding:
Paperback
Udgave:
ISBN-10:
1607410710
Udg. Dato:
21 maj 2010
Længde:
7mm
Bredde:
153mm
Højde:
229mm
Forlag:
Nova Science Publishers Inc
Oplagsdato:
21 maj 2010
Forfatter(e):
Finder produkter...
Kategori sammenhænge